DON: XPD Pattern

Framework Type DON

Powder Diffraction Pattern for edited data of UTD-1F

Modify the data as desired and then press the submit button

Warning: no checking is performed. Please make sure that the data entered are sensible

	Material name
	Original composition
	Refined composition
	Edited composition

Space group:		Setting:
Unit cell:	a = Å	b = Å	c = Å
	α = °	β = °	γ = °

Atomic coordinates:

Atom name

Form factor

B(iso)

Si1    Si    0.096    0.18    0.1066    1    0.95 
Si2    Si    0.076    0.313    0.1986    1    0.95 
Si3    Si    0.124    0.18    0.2943    1    0.95 
Si4    Si    0.24    0.305    0.3824    1    0.95 
Si5    Si    0.41    0.176    0.4374    1    0.95 
Si6    Si    0.608    0.306    0.4689    1    0.95 
Si7    Si    0.793    0.183    0.4654    1    0.95 
Si8    Si    0.912    0.307    0.3992    1    0.95 
Si9    Si    0.929    0.182    0.3045    1    0.95 
Si10    Si    0.868    0.309    0.2072    1    0.95 
Si11    Si    0.769    0.176    0.1199    1    0.95 
Si12    Si    0.585    0.308    0.0659    1    0.95 
Si13    Si    0.398    0.19    0.04    1    0.95 
Si14    Si    0.206    0.316    0.041    1    0.95 
Si15    Si    0.902    0.318    0.0631    1    0.95 
Si16    Si    0.108    0.18    0.4432    1    0.95 
Si17    Si    0.081    0.816    0.1046    1    0.95 
Si18    Si    0.076    0.675    0.1994    1    0.95 
Si19    Si    0.127    0.807    0.2936    1    0.95 
Si20    Si    0.239    0.678    0.3836    1    0.95 
Si21    Si    0.418    0.808    0.4366    1    0.95 
Si22    Si    0.604    0.687    0.4663    1    0.95 
Si23    Si    0.798    0.81    0.4672    1    0.95 
Si24    Si    0.914    0.679    0.4024    1    0.95 
Si25    Si    0.931    0.797    0.3052    1    0.95 
Si26    Si    0.867    0.67    0.2096    1    0.95 
Si27    Si    0.762    0.809    0.1211    1    0.95 
Si28    Si    0.587    0.313    0.5659    1    0.95 
Si29    Si    0.386    0.181    0.5374    1    0.95 
Si30    Si    0.194    0.685    0.04    1    0.95 
Si31    Si    0.89    0.318    0.5625    1    0.95 
Si32    Si    0.11    0.808    0.4458    1    0.95 
O1    O    0.169    0.278    0.0863    1    0.32 
O2    O    0.108    0.208    0.1608    1    0.32 
O3    O    0.131    0.265    0.2484    1    0.32 
O4    O    0.101    0.494    0.1903    1    0.32 
O5    O    0.209    0.23    0.3331    1    0.32 
O6    O    0.033    0.23    0.3097    1    0.32 
O7    O    0.125    0.995    0.287    1    0.32 
O8    O    0.348    0.283    0.3979    1    0.32 
O9    O    0.191    0.22    0.4183    1    0.32 
O10    O    0.215    0.491    0.3798    1    0.32 
O11    O    0.513    0.23    0.443    1    0.32 
O12    O    0.375    0.202    0.4835    1    0.32 
O13    O    0.689    0.237    0.4472    1    0.32 
O14    O    0.624    0.264    0.5218    1    0.32 
O15    O    0.601    0.496    0.4626    1    0.32 
O16    O    0.851    0.21    0.4274    1    0.32 
O17    O    0.839    0.279    0.5109    1    0.32 
O18    O    0.89    0.251    0.3468    1    0.32 
O19    O    0.797    0.997    0.4778    1    0.32 
O20    O    0.887    0.494    0.402    1    0.32 
O21    O    0.87    0.253    0.2581    1    0.32 
O22    O    0.919    0.99    0.3025    1    0.32 
O23    O    0.797    0.197    0.1738    1    0.32 
O24    O    0.967    0.294    0.195    1    0.32 
O25    O    0.831    0.489    0.2009    1    0.32 
O26    O    0.664    0.227    0.1035    1    0.32 
O27    O    0.833    0.285    0.0962    1    0.32 
O28    O    0.489    0.247    0.0739    1    0.32 
O29    O    0.598    0.741    0.5166    1    0.32 
O30    O    0.59    0.502    0.5718    1    0.32 
O31    O    0.314    0.288    0.0503    1    0.32 
O32    O    0.382    0.996    0.5496    1    0.32 
O33    O    0.186    0.499    0.0267    1    0.32 
O34    O    0.112    0.995    0.0982    1    0.32 
O35    O    0.853    0.725    0.5119    1    0.32 
O36    O    0.994    0.221    0.0794    1    0.32 
O37    O    0.929    0.497    0.5648    1    0.32 
O38    O    0.019    0.282    0.4218    1    0.32 
O39    O    0.14    0.216    0.497    1    0.32 
O40    O    0.146    0.707    0.0822    1    0.32 
O41    O    0.095    0.78    0.1582    1    0.32 
O42    O    0.14    0.73    0.2469    1    0.32 
O43    O    0.212    0.756    0.334    1    0.32 
O44    O    0.034    0.75    0.3059    1    0.32 
O45    O    0.346    0.7    0.4027    1    0.32 
O46    O    0.185    0.76    0.4177    1    0.32 
O47    O    0.518    0.757    0.4306    1    0.32 
O48    O    0.406    0.218    0.988    1    0.32 
O49    O    0.401    0.992    0.4223    1    0.32 
O50    O    0.695    0.749    0.4535    1    0.32 
O51    O    0.848    0.78    0.4262    1    0.32 
O52    O    0.903    0.736    0.3507    1    0.32 
O53    O    0.864    0.721    0.2612    1    0.32 
O54    O    0.799    0.786    0.1748    1    0.32 
O55    O    0.969    0.689    0.2014    1    0.32 
O56    O    0.655    0.232    0.6092    1    0.32 
O57    O    0.817    0.305    0.5948    1    0.32 
O58    O    0.78    0.991    0.1064    1    0.32 
O59    O    0.484    0.252    0.5629    1    0.32 
O60    O    0.303    0.269    0.5536    1    0.32 
O61    O    0.975    0.203    0.5788    1    0.32 
O62    O    0.153    0.211    0.9993    1    0.32 
O63    O    0.083    0.993    0.4353    1    0.32 
O64    O    0.019    0.702    0.4307    1    0.32 
Co1    Co    0.502    0.258    0.2542    1    1.82 
C1    C    0.518    0.06    0.218    1    5.53 
C2    C    0.577    0.054    0.262    1    5.53 
C3    C    0.523    0.062    0.295    1    5.53 
C4    C    0.429    0.071    0.271    1    5.53 
C5    C    0.426    0.07    0.224    1    5.53 
C6    C    0.558    0.063    0.346    1    11.05 
C7    C    0.681    0.03    0.271    1    11.05 
C8    C    0.546    0.05    0.172    1    11.05 
C9    C    0.34    0.07    0.186    1    11.05 
C10    C    0.347    0.068    0.294    1    11.05 
C11    C    0.543    0.45    0.222    1    5.53 
C12    C    0.584    0.453    0.27    1    5.53 
C13    C    0.512    0.457    0.294    1    5.53 
C14    C    0.427    0.456    0.262    1    5.53 
C15    C    0.446    0.452    0.217    1    5.53 
C16    C    0.525    0.473    0.345    1.5    11.05 
C17    C    0.686    0.457    0.291    1.5    11.05 
C18    C    0.594    0.456    0.184    1.5    11.05 
C19    C    0.376    0.462    0.172    1.5    11.05 
C20    C    0.333    0.466    0.272    1.5    11.05

Input Profile Parameters

	Wavelength:	or
	2θ range:	° - °
	Step size:	°2θ
	Polarization factor:
	Background:
	Reference peak is	highest peak in 2θ range
		peak closest to °2θ
		reflection (hkl)
	scaled to
	Intensity axis:	-

Peak shape
	Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
	FWHM = sqrt (U + V tan θ + W tan²θ)
	Mixing parameter (n):	%
	Peak range:	FWHM
	Peak width:
	set UVW at:	U = V = W =
	Calculate UVW such that	FWHM = at °2θ
		FWHM = at °2θ
		FWHM = at °2θ

Select Output

List hkl and intensity

List powder pattern

plot powder pattern